Carbon Hybrid Plate 2.0mm
| Quantity | Unit price |
|---|---|
| To 9 |
€51.21*
|
| To 49 |
€48.65*
|
| From 50 |
€46.09*
|
available immediately
Product information "Carbon Hybrid Plate 2.0mm"
Our carbon hybrid panels are manufactured using the thermal high-pressure hot-press process and therefore have a high fiber volume content of >65%. An epoxy resin matrix serves as the matrix material. The carbon hybrid plates are made entirely of carbon fabric with top layers of an aluminized hybrid fabric. The fiber structure has a homogeneous, biaxial fiber distribution in 0°/90°.
The hybrid fabric of the outer layers is made in a twill weave, has a smooth, milled surface and has the typical visible fabric structure.
Due to the high pressing pressure during the manufacturing process, these carbon hybrid plates achieve outstanding properties in the area of flexural strength as well as torsional and dimensional stability.
The panels have the following characteristic laminate values:
Flexural strength EN2562: 820 MPa
Flexural modulus EN2562: 55 GPa
Tensile strength ISO 527: 630 MPa
Tensile modulus of elasticity ISO 527: 58 GPa
Coefficient of thermal expansion: 1 E^-06 1/K
I.L.S.S. EN2563: ~68MPa
Density: 1.6 g/cm³
Fiber weight percentage: >65%
Glass transition temperature (short term): 130°C (180°C)
Water absorption: < 0.04%