Hybrid Plate 0.3mm

Product information "Hybrid Plate 0.3mm"

Hybrid panels are manufactured using the thermal high-pressure hot-press process and therefore have a high fiber volume content of >65%. An epoxy resin matrix serves as the matrix material. Hybrid panels are particularly suitable for design applications. Its surface is smooth and the aluminized fabric gives it a metallic carbon design look. The fiber structure shows a homogeneous, biaxial fiber distribution in 0°/90°.

We offer the pure hybrid plates in thicknesses of around 0.3mm and 0.5mm, which means that they are still somewhat flexible and adapt to contours.

The following characteristic laminate values apply to hybrid panels:

Flexural strength EN2562: 370 MPa
Flexural modulus EN2562: 24 GPa
Tensile strength ISO 527: 260 MPa
Tensile modulus of elasticity ISO 527: 58 GPa
Density: 2 g/cm³
Fiber weight percentage: >65%
Glass transition temperature (short term): 130°C (180°C)
Water absorption: < 0.04%